Semiconductor structure and manufacturing method thereof

ABSTRACT

A semiconductor structure includes a surface having a plurality of portions and a dielectric material over the surface. The dielectric material includes an aspect ratio substantially equal to or greater than a predetermined value.

FIELD

The disclosure relates to a semiconductor structure, and more particularly to a semiconductor structure with a dielectric material.

BACKGROUND

Semiconductor devices are widely used in different fields as costs and physical dimensions reduce with advancing technologies. Structures of semiconductor devices become more and more complicated because transistor density per unit area increases. Multilevel of conductive pattern features are also adopted to improve performance of semiconductor devices.

Dielectric material is adopted as a structure in semiconductor devices to isolate transistors in different regions. Dielectric material is also utilized to separate conductive patterns located in different levels. As the geometry shrinks, a multi-step method is used to grow the dielectric material in a multi-layer manner. However, the interface between each layer is a weak point of the dielectric material.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, some features are not drawn to scale. In fact, the dimensions of the some features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 is a schematic of a semiconductor structure, in accordance with some embodiments of the present disclosure

FIG. 2 is a fluorine concentration distribution in a dielectric material of the structure in FIG. 1, according to some embodiments of the present disclosure.

FIGS. 3A-3G are schematic diagrams illustrating a method of manufacturing the semiconductor structure in FIG. 1 at an STI stage, according to some embodiments of the present disclosure.

FIG. 4 is an exemplary semiconductor structure at an ILD stage, according to some embodiments of the present disclosure.

FIG. 5 is a fluorine and phosphorous concentration distribution of a dielectric material in the structure of FIG. 4, according to some embodiments of the present disclosure.

FIGS. 6A-6H are schematic diagrams illustrating a method of manufacturing the semiconductor structure in FIG. 5 at an ILD stage, according to some embodiments of the present disclosure.

FIG. 7 is an exemplary semiconductor structure at an IMD stage, according to some embodiments of the present disclosure.

FIG. 8 is a fluorine concentration distribution of a dielectric material of the structure in FIG. 7, according to some embodiments of the present disclosure.

FIGS. 9A-9E are schematic diagrams illustrating a method of manufacturing the semiconductor structure in FIG. 8 at IMD stage, according to some embodiments of the present disclosure.

DETAILED DESCRIPTION OF THE INVENTION

According to the present disclosure, a dielectric material is introduced in a semiconductor structure. The dielectric material is arranged as a gap filling film between pattern features in some stages. In some embodiments, the dielectric material acts as an isolation filled in a trench of a substrate. In some embodiments, the dielectric material acts as an isolation between conductive lines. The conductive lines are electrically conductive or semi-conductive.

In some embodiments of the present disclosure, concentration of phosphorus is substantially constant across the dielectric material. In some embodiments, fluorine concentration changes in a substantially linear manner across the dielectric material. In some embodiments, the dielectric layer is a portion of the dielectric material.

In the present disclosure, some exemplary stages are used to illustrate some embodiments. A shallow trench isolation (STI) stage refers to a stage in which STI structures are defined. The STI structures are designed to isolate transistor gates, sources, drains, etc. An inter layer dielectric (ILD) stage is in between formation of a transistor gate and formation of a first metal layer. An IMD stage is after the ILD stage.

Semiconductor Structure at STI Stage

FIG. 1 is an exemplary semiconductor structure 100 at an STI stage, in accordance with some embodiments. A semiconductor substrate 120 of the semiconductor structure 100 provides a foundation to form semiconductor circuitry. In some embodiments, the substrate 120 is a silicon substrate with a first conductivity type, which is a p-type, for example. In some embodiments, the substrate 120 has several doped regions. Some of the doped regions have a second conductivity type opposite to the first conductivity type. Some of the doped regions have the first conductivity type with a higher concentration than that of the substrate 120. The semiconductor substrate 120 has a surface 122 (not labeled in the drawing) that includes two portions 122A, two portions 122C, and a portion 122B. The surface 122 is a jagged surface and is illustrated by a coarse line in FIG. 1. Each portion 122C is in between a corresponding portion 122A and the portion 122B. The portion 122B is connected with two portions 122C.

A liner 125 is disposed on the surface 122. As illustratively shown in FIG. 1, the liner 125 is disposed on the portion 122B and two portions 122C of the surface 122. In some embodiments not shown in FIG. 1, the liner 125 is also disposed on two portions 122A. The liner 125 has a thickness D between about 50 Å and 700 Å. In some embodiments, the liner 125 is electrically isolative.

A dielectric material 127 is disposed on the liner 125. In some other embodiments that there is not the liner 125, the dielectric material 127 is directly disposed on the portion 122B and two portions 122C. The dielectric material 127 has a predetermined shape, which is determined by the portion 122B and two portions 122C. As illustratively shown in FIG. 1, the dielectric material 127 has a shape of a trapezoid. In some other embodiments, the dielectric material 127 has a shape of a quadrilateral. Other shapes of the dielectric material 127 are within the contemplated scope of the present disclosure.

The dielectric material 127 has predetermined dimensions, such as a first width W₁, a second width W₂ and a height H. As shown in FIG. 1, the width W₁ is defined by a corner 132 and a corner 134 of the dielectric material 127. The width W₂ is defined by a corner 136 and a corner 137 of the dielectric material 127. The height H is defined by a top surface 130 of the dielectric material 127 and a bottom surface 131 of the dielectric material 127. In FIG. 1, the bottom surface 131 is an interface between the dielectric material 127 and the liner 125. The dielectric material 127 has an aspect ratio, which is defined by a ratio of the height H over the width W₁ of the dielectric material 127. In some embodiments, the height H is greater than 72 nm and the width W is smaller than 30 nm. As a result, the aspect ratio of the dielectric material 127 is 2.4. In some embodiments, the aspect ratio of the dielectric material 127 is greater than 2.4, and is, for example, 2.8, 3.5, etc. In some embodiments, such as a 40 nm CMOS (complimentary metal oxide semiconductor) device, the aspect ratio of the dielectric material 127 in the STI stage is greater than 2.4 in order to meet the design rule. Other values of the aspect ratio are within the contemplated scope of the present disclosure.

The dielectric material 127 has a silicon glass matrix and electrically isolates active regions in the substrate 120. In some embodiments with references to FIG. 1, the dielectric material 127 has a fluorine ion in the silicon glass matrix. FIG. 2 is a graph representing fluorine concentration distribution in the dielectric material 127 according to some embodiments. The fluorine concentration is measured by a secondary ion mass spectrometer (SIMS), an Auger electron nanoscope (Auger) or other suitable analysis tools. In FIG. 2, the Y-axis represents the fluorine concentration in atomic ratio per cubic centimeters (Atoms/cm³). The X-axis represents a depth of the dielectric material 127 that is referenced from the top surface 130 of the dielectric material 127, and the unit is Å.

In the illustration of FIG. 2, the dielectric material 127 has a depth of about 1000 Å. The depth is also the height H of the dielectric material 127 shown in FIG. 1. The fluorine concentration is thus illustrated from 0 Å to about 1000 Å. From 0 Å to about 1000 Å, the fluorine concentration changes from about 1×E20 Atoms/cm³ to about 2×E20 Atoms/cm³. Effectively, the fluorine concentration is lowest at the surface 130 and is highest at the interface 131.

FIGS. 3A-3G are cross sectional views of the semiconductor structure 100 at the STI stage illustrated in FIG. 1, according to some embodiments of the present disclosure.

In FIG. 3A, a substrate 120 having a surface 121 is provided. In FIG. 3B, a portion of the substrate 120 is removed to form a trench in the substrate 120. Two portions labeled 122A are remaining portions of the surface 121 in FIG. 3B. Two sidewalls of the trench correspond to two portions 122C in FIG. 1. A bottom surface of the trench corresponds to the portion 122B in FIG. 1. Two portions 122A, two portions 122C and portion 122C form the surface 122 in FIG. 1. The trench has a height H′ defined as a distance from the surface portion 122A and the surface portion 122B.

In FIG. 3C, a layer 125A is formed on the surface 122. The layer 125A has a thickness D referenced from the bottom of the trench. In FIG. 3D, a dielectric layer 127-1 is formed on the layer 125A. Effectively, the dielectric layer 127-1 is also formed over the surface 122. In some embodiments without the liner 125, the dielectric layer 127-1 is formed on the surface 122. The dielectric layer 127-1 has a thickness h₁.

A chemical vapor deposition (CVD) process is used to form the dielectric layer 127A. In some embodiments, the CVD process is a high density plasma (HDP) or high aspect ratio process (HARP). The CVD process includes a deposition step and an insitu sputter step. The deposition step is to form some dielectric material in the trench and the insitu sputter step uses ions such as argon ions to remove a portion of the dielectric material. The dielectric layer 127-1 in FIG. 3D is a final profile formed by the CVD process. The dielectric layer 127-1 has two overhangs 127-1 a.

In FIG. 3E, an insitu etch step is used to remove a portion of the dielectric layer 127-1. During this operation, the overhangs 127-1 a in FIG. 3D are removed. In some embodiments as illustrated with reference to FIG. 3E, an NF₃ gas is ionized to remove the portion of the dielectric layer 127-1. A circle with an “F” represents a fluorine ion of the ionized NF3 gas. The thickness of the dielectric layer 127-1 is reduced to h₁′. In some embodiments, the thickness h₁′ is about ⅙ of the height H. The height H is defined by a surface portion 122A and the interface between the dielectric layer 127-1 and the liner 125.

In FIG. 3F, an operation to treat a top surface of the dielectric layer 127-1 with plasma is illustrated. In this operation, a gas is introduced and ionized by a first radio frequency (RF) power to form the plasma. In some embodiments, the gas is oxygen and the first RF power is between about 1000 W and 9000 W. A circle with an “O” illustrates an oxygen ion. A second RF power is also introduced to accelerate the plasma to treat the top surface of the dielectric layer 127-1. In some embodiments, the second RF power is between about 1000 W and 9000 W. During this operation, fluorine concentration at the top surface of the dielectric layer 127-1 is adjusted. The fluorine concentration in the dielectric layer 127-1 changes in a linear manner.

In some embodiments, several cycles are used to form the dielectric material 127 to a predetermined thickness. For example, operations with reference to FIGS. 3D to 3F are repeated to form a cycle of forming the dielectric layer 127-1. In some embodiments as illustrated in FIG. 3G, an operation that repeats the cycle 6-7 times is used to form the dielectric material 127 in the trench having the thickness H. A portion of the layer 125A in FIG. 3F is also removed to result in the liner 125.

Semiconductor Structure at ILD Stage

FIG. 4 is an exemplary semiconductor structure 400 at an ILD stage, in accordance with some embodiments. The semiconductor structure 400 has a surface 122-1 (not labeled in the drawing) and two conductors 150 on the substrate 120. The surface 122-1 includes at least two portions 122-1A, two portions 122-1C, and a portion 122-1B. The portion 122-1A, 122-1B, and 122-1C correspond to the portion 122A, 122B, and 122C in FIG. 1, respectively. The conductors 150 are electrically conductive and, in some embodiments, are gates of the semiconductor structure 400. The two conductors 150 are identical, and the conductor 150 on the right side is used in the exemplary illustration that is also applicable to the other conductor 150. A portion 122-1C is a sidewall of the conductor 150 and a portion 122-1A is a top surface of the conductor 150. A first spacer 123A is adjacent to a sidewall of the conductor 150. A second spacer 123B is adjacent to the first spacer 123A. Spacers 123A and 123B are symmetrical with reference to the conductor 150. In some embodiments, the semiconductor structure 400 has at least one spacer at each side of the conductor 150.

A liner 125A is disposed over the substrate 120 and other locations. For example, a portion of the liner 125A is over the conductors 150, another portion is on the top surface 122-1A of the conductor 150, and another portion is on the spacers 123A and 123B. In some embodiments, the liner 125A is an etch stop layer.

A dielectric material 127A corresponds to the dielectric material 127 in FIG. 1, and includes phosphorous ions in addition to fluorine ions as in the dielectric material 127. The dielectric material 127A also has a silicon glass matrix and electrically isolates the conductors 150.

FIG. 5 is a fluorine concentration distribution of the dielectric material 127A in FIG. 4 according to some embodiments. The fluorine concentration is measured by a secondary ion mass spectrometer (SIMS), an Auger electron nanoscope (Auger) or other suitable analysis tools. In FIG. 5, the Y-axis represents the fluorine concentration and the unit is atomic ratio per cubic centimeters (atoms/cm³). The X-axis represents a depth of the dielectric material 127A with reference to a line AA′ in FIG. 4, and the unit is Å. Line 501 represents the fluorine concentration versus the depth of the dielectric material 127A. In the illustration of FIG. 5, the dielectric material 127A has a depth of about 1000 Å. The depth is also the height H of the dielectric material 127A. The fluorine concentration is thus illustrated from 0 Å to about 1000 Å. From 0 Å to about 1000 Å, the fluorine concentration changes from about 1×E20 Atoms/cm³ to about 2×E20 Atoms/cm³. Effectively, the fluorine concentration is lowest at the surface 130 shown in FIG. 4 and is highest at the interface 131.

Line 502 represents the phosphorous concentration distribution versus the depth of the dielectric material 127A. In FIG. 5, the phosphorous concentration is substantially constant in the dielectric material 127A.

FIGS. 6A-6H are cross sectional views of the semiconductor structure 400 at the ILD stage illustrated in FIG. 4, according to some embodiments of the present disclosure.

In FIG. 6A, two conductors 150 are formed on the surface 121 of the substrate 120. Each conductor 150 includes a sidewall 122-1C. The top surface of each conductor 150 corresponds to the portion 122-1A in FIG. 4. A portion of the surface 121 between the two conductors 150 corresponds to the portion 122-1B in FIG. 4.

In FIG. 6B, a first spacer 123A is formed on a corresponding sidewall 122-1C of the conductors 150. In FIG. 6C, a second spacer 123B is formed adjacently to the first spacer 123A. For simplicity, only elements associated with one conductor 150 are labeled.

In FIG. 6D, a liner 125A is formed and covers the top surface 122-1A of the conductor 150 and on the spacers 123A and 123B. A portion of the liner 125A is on the bottom surface 122-1B. An opening 126 between the conductors 150 has a height H and a width W.

In FIG. 6E, a doped chemical vapor deposition (CVD) process is used to form a dielectric layer 127A-1 on the liner 125A. In some embodiments, the doped CVD process is a high density plasma (HDP) or HARP process. The dopant is phosphorous ions. The doped chemical vapor deposition includes a deposition step and an insitu sputter step. The deposition step forms doped dielectric material on the liner 125A. The insitu sputter step uses ion such as argon ions and removes a portion of the doped dielectric material.

A same fluorine ion etch process as illustrated in FIG. 3E is adopted to remove the overhangs 127A-1 a after the operation in FIG. 6E. FIG. 6F illustrates the height of dielectric layer 127A-1 is reduced to h₁′.

In FIG. 6G, an operation to treat a top surface of the dielectric layer 127A-1 with plasma is illustrated. For some embodiments, a PH₃ gas is introduced and ionized by a first radio frequency (RF) power to form the plasma. Phosphorous ions are generated from the ionized PH₃ gas. A circle with an “P” illustrates an phosphorous ion. A second RF power is also introduced to accelerate the plasma to treat the top surface of the dielectric layer 127A-1. The magnitude of the first and the second RF powers are as illustrated with reference to FIGS. 3A-3G. During the first and second RF operations, phosphorous concentration at the top surface of the dielectric layer 127A-1 is adjusted. The phosphorous concentration in the dielectric layer 127A-1 is substantially constant throughout the dielectric layer 127A-1. Fluorine concentration at the top surface of the dielectric layer 127A-1 is adjusted to change in a linear manner throughout the dielectric layer 127A-1.

In some embodiments, several cycles are used to form the dielectric material 127A to a predetermined height. For example, operations with reference to FIGS. 6E to 6G are repeated as a cycle to form the dielectric layer 127A-1. An operation that repeats the cycle 6-7 times is used and results in the dielectric material 127A having the height H.

Semiconductor Structure at IMD Stage

FIG. 7 is an exemplary semiconductor structure 700 at an IMD stage, in accordance with some embodiments. The semiconductor structure 700 has a surface 122-2 not labeled in the drawing) and two conductors 160 on a substrate 120A. The surface 122-2 includes at least two portions 122-2A two portions 122-2C and a portion 122-2B. The portion 122-2A, 122-2B, and 122-2C correspond to the portion 122A, 122B, and 122C in FIG. 1, respectively. In some embodiments, the conductors 160 include metal. The substrate 120A corresponds to the substrate 120 in FIG. 1, and, in addition to silicon, also includes metal and dielectric.

A dielectric material 127 is on the portions 122-2C and the portion 122-2B. In some embodiments, a liner 125A (not shown in the drawing) is between the dielectric material 127 and the surface 122-2. The dielectric material 127 has a fluorine ion in the silicon glass matrix. The dielectric material 127 has a height H. In some embodiments, the height of the dielectric material 127 is dependant on a height of the conductor 160.

FIG. 8 is a fluorine concentration distribution in the dielectric material 127 according to some embodiments. The X-axis represents a depth of the dielectric material 127 with reference to a line AA′ in FIG. 7, and the unit is Å. Line 801 represents the fluorine concentration versus the depth of the dielectric material 127.

In the illustration of FIG. 8, the dielectric material 127 has a depth of about 1000 Å. The depth is also the height H of the dielectric material 127. For the embodiments as illustrated in FIG. 8, the fluorine concentration is thus illustrated from 0 Å to about 1000 Å, which is substantially equal to the height H of the dielectric material 127. Other values of the height are within the contemplated scope of the present disclosure. From 0 Å to about 1000 Å, the fluorine concentration changes from about 1×E20 Atoms/cm³ to about 2×E20 Atoms/cm³. Effectively, the fluorine concentration is lowest at the surface 130 and is highest at the portion 122-2B.

FIGS. 9A-9E are cross sectional views of the semiconductor structure 700 at the IMD stage illustrated in FIG. 7, according to some embodiments of the present disclosure.

In FIG. 9A, two conductors 160 are formed on a surface 121 of a substrate 120A. In some embodiments with referenced to FIG. 9A, the conductor 150 has a shape of a trapezoid. In FIG. 9B, a CVD process is used to form a dielectric layer 127-1 on the portions 122-2A, 122-2B and 122-2C. In some embodiments, the CVD process is a HDP or HARP process. Two overhangs 127-1 a are formed on top corners 164 of the conductors 160.

A same fluorine ion etch process illustrated in FIG. 3E is adopted to remove the overhangs 127-1 a. The thickness of the dielectric layer 127-1 is reduced to h₁′ as illustrated in FIG. 9C.

FIG. 9D is used to illustrate an operation to treat a top surface of the dielectric layer 127-1 with plasma. In some embodiments with reference to FIG. 9D, the plasma includes oxygen ions.

In some embodiments, several cycles are used to form the dielectric material 127 to a predetermined height. For example, operations with reference to FIGS. 9B to 9D are repeated to form a cycle to form the dielectric layer 127-1. In some embodiments as illustrated in FIG. 9E, an operation that repeats the cycle 6-7 times is used to form the dielectric material 127 having the thickness H.

In some embodiments, a semiconductor structure includes a surface having a plurality of portions and a dielectric material over the surface. The dielectric material includes an aspect ratio that is substantially equal to or greater than a predetermined value.

In some embodiments, a semiconductor structure includes conductors and a spacer disposed on a sidewall of each conductor of the conductors. The semiconductor structure has a liner on the spacer and a top surface of each conductor of the conductors. The semiconductor structure also has a phosphorous doped dielectric material between two conductors and the phosphorous concentration throughout the phosphorous doped dielectric material is substantially constant.

In some embodiments, a method of manufacturing a semiconductor structure includes forming a surface, forming a dielectric layer over the surface, etching the dielectric layer, and treating a top surface of the dielectric layer with plasma.

The above description includes exemplary operations, but these operations are not necessarily required to be performed in the order shown. Operations may be added, replaced, changed order, skipped, and/or eliminated as appropriate, in accordance with the spirit and scope of the disclosure. Accordingly, the scope of the disclosure should be determined with reference to the following claims, along with the full scope of equivalences to which such claims are entitled. 

What is claimed is:
 1. A semiconductor structure, comprising: a surface including a plurality of portions; a dielectric material over the surface, wherein the dielectric material includes an aspect ratio that is substantially equal to or greater than a predetermined value.
 2. The semiconductor structure of claim 1, further comprising a liner between a portion of the plurality of portions and the dielectric material.
 3. The semiconductor structure of claim 1, wherein the dielectric material includes an impurity having a concentration distributed in a linear manner throughout the dielectric material.
 4. The semiconductor of claim 3, wherein the impurity includes fluorine.
 5. The semiconductor structure of claim 1, wherein the dielectric material has an impurity with a concentration substantially constant throughout the dielectric material.
 6. The semiconductor of claim 5, wherein the impurity includes phosphorous.
 7. The semiconductor of claim 1, further comprising a plurality of conductors wherein each of the conductors includes a sidewall that is a portion of the surface.
 8. A semiconductor structure, comprising: a plurality of conductors; a spacer disposed on a sidewall of each of the plurality of conductors; a liner on the spacer and a surface of each of the plurality of conductors; and a phosphorous doped dielectric material between two conductors of the plurality of conductors, wherein a phosphorous concentration throughout the phosphorous doped dielectric material is substantially constant.
 9. The semiconductor structure of claim 8, wherein the phosphorous doped dielectric material includes a thickness substantially equal to a height of the plurality of conductors.
 10. The semiconductor structure of claim 8, wherein the phosphorous doped dielectric material includes an aspect ratio equal to or greater than about 2.4.
 11. The semiconductor structure of claim 8, wherein the dielectric material has a width smaller than 30 nm.
 12. The semiconductor structure of claim 8, wherein the phosphorous doped dielectric material further comprises fluorine.
 13. The semiconductor structure of claim 12, wherein a fluorine concentration is distributed in a linear manner throughout the phosphorous doped dielectric material.
 14. The semiconductor structure of claim 12, wherein a fluorine concentration is highest at an interface between the phosphorous doped dielectric material and the liner.
 15. A method of manufacturing a semiconductor structure, comprising: forming a surface on substrate; forming a dielectric layer over the surface; etching the dielectric layer; and treating a top surface of the dielectric layer with plasma.
 16. The method of claim 15, wherein treating the top surface of the dielectric layer is with phosphorous plasma.
 17. The method of claim 15, wherein treating the top surface of the dielectric layer is with oxygen plasma.
 18. The method of claim 15, wherein etching the dielectric layer is an NF₃ etch.
 19. The method of claim 15, further comprising repeating forming the dielectric layer.
 20. The method of claim 15 further comprising forming a liner between the surface and the dielectric layer. 